Evolution of Microstructure during Welding Simulation of Boron Modified P91 Steel

Formation of heat affected zone (HAZ) when welding is considered as weakest link across transition joint. Characterization of this zone is a key issue to reduce the effect of embrittlement; hence appropriate welding parameters were adopted. In the present study, HAZ simulation was done for boron modified P91 steel using Gleeble. It has been observed that matrix was martensitic in nature for coarse-grain HAZ (CGHAZ)/fine-grain HAZ (FGHAZ) whereas...