Cyclic plastic deformation behaviour of a directionally solidified nickel base superalloy at 850 °C: Damage micromechanisms

Dislocation based deformation micromechanisms during low cycle fatigue deformation of nickel base superalloy CM 247 DS LC at 850 °C was investigated by conducting fatigue tests employing constant strain amplitudes for strain ratio (R) values of 0, −1 and carrying out extensive SEM and TEM examinations. Cyclic life of the alloy reduces for all fatigue tests conducted employing R = 0 in comparison with R = −1 owing to sustained mean stress...