Experimental investigation of kink initiation and kink band formation in unidirectional glass fiber-reinforced polymer specimens

The failure mechanism of non-slender glass fiber-reinforced epoxy prismatic specimens subjected to axial compression and different temperatures was investigated. Digital image correlation was used to map and derive the failure modes. The failure mode changed from splitting failure at ambient temperature to kinking at the onset of the glass transition temperature. The kink initiation mechanism could be clearly observed. Based on the initial...