Damage accumulation during high temperature fatigue of Ti/SiCf metal matrix composites under different stress amplitudes

The damage mechanisms and load redistribution taking place under high temperature (350 °C), high cycle fatigue (HCF) of TC17 titanium alloy/unidirectional SiC fibre composites have been investigated in situ using synchrotron X-ray computed tomography (CT) and X-ray diffraction (XRD) under two stress amplitudes. The three-dimensional morphology of the fatigue crack and fibre fractures has been mapped by CT. At low stress amplitude, stable growth...