Background . The development of dental caries is associated with various microorganisms and secondary caries formation is the main cause of restorations failure. The advice for restorative dental materials that have antimicrobial properties has stimulated the introduction of materials containing different antibacterial agents. Objectives . The present study has been designed to synthesize silver nanoparticles (AgNPs) and incorporate AgNPs and amoxicillin into glass ionomer cement (GIC) to synergize its effect on oral microbes. The effect of the added antimicrobial agents on compressive strength (CS) of GIC was also evaluated. Material and methods . Biosynthesis of AgNPs was done using Cupressus macrocarpa extract and AgNPs were characterized. A total of 120 disc-shaped specimens were prepared and classified into 4 main groups where Group A includes conventional GIC, Groups B and C include GIC with AgNPs or amoxicillin, respectively, while Group D included GIC with both AgNPs and amoxicillin. Each group was tested for the antimicrobial activity against both Streptococcus mutans ( S. mutans ) and Staphylococcus aureus ( S. aureus ). The distribution of biofilm was examined via a scanning electron microscope. The CS of the tested material was measured using a Material Test System. Results . The UV−visible spectrum showed a peak of 429 nm. Transmission electron microscopy, x-ray diffraction pattern and Fourier transform infrared analysis confirmed the formation of AgNPs with spherical to oblong polydispersed particles of diameter in the range of 13.5–25.8 nm. The maximum inhibitory zone was recorded for group D against both tested bacteria with a mean of 29 mm at first 24 h period to 15 mm at three weeks and showed antimicrobial rate 92.2% and 92.56%, against both strains, respectively. Additionally, group D disintegrated the structure of S. aureus biofilm and even kill bacteria in the biofilms. The addition of AgNPs and amoxicillin caused an insignificant effect on CS of GIC. Conclusion. TheAgNPs showed a synergistic effect in combination with amoxicillin and GIC dental restorative material against studied microorganisms. The agents can be safely added with minimal effect on the mechanical properties of the original cement.

Antimicrobial activity of biosynthesized silver nanoparticles, amoxicillin, and glass-ionomer cement against Streptococcus mutans and Staphylococcus aureus