Radiation response of a Fe–20Cr–25Ni austenitic stainless steel under Fe2+ irradiation at 500 °C

The radiation response of a Fe–20Cr–25Ni austenitic stainless steel under self-ion irradiation at 500 °C was systematically investigated. The steel was irradiated at 500 °C by 3.5 MeV Fe2+ ions to 10, 50, and 150 peak dpa, respectively. In the 200–400 nm depth region, radiation-induced Frank loops were relatively stable in both size and number density from 10 to 150 peak dpa. Anisotropic distribution of Frank loops was observed in the 50 and 150...