Influence of Sintering Temperature on Microstructure and Mechanical Properties of Ti–Mo–B4C Composites

Ti–10 wt% Mo–1 wt% B4C composite samples were SPSed under the circumstances of 5 min dwell time, 50 MPa external pressure and sintering temperatures of 1150 °C, 1300 °C and 1450 °C. The role of sintering temperature on the relative density, microstructure and mechanical characteristics of as-sintered specimens were studied. Near fully dense relative density was obtained for the samples sintered at 1450 °C. The best mechanical properties...