Comparison of the mechanical properties of translucent zirconia and lithium disilicate
Abstract
Three mol% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) possesses excellent mechanical properties but is relatively opaque. Five mol% yttria-stabilized zirconia polycrystal (5Y-ZP) offers improved translucency, but many of its clinical properties have not been compared with those of 3Y-TZP and lithium disilicate . The purpose of this in vitro study was to compare the flexural strength , translucency parameter, bond strength , and enamel and material wear of 5Y-ZP (Katana UTML) with 3Y-TZP (Katana HT) and lithium disilicate (e.max CAD). Flexural strength bars were sectioned (n=10, 25×4×2 mm), sintered or crystallized, polished, and fractured at 1 mm/min. Translucency specimens (1 mm thick) were fabricated (n=10). Their L*a*b* values were measured against a black-and-white background with a spectrophotometer, and ΔE 00 was calculated. Zirconia bond strength specimens were airborne-particle abraded with 50 μm alumina followed by the application of a 10-methacryloxydecyl dihydrogen phosphate–containing primer (Clearfil Ceramic Primer). Lithium disilicate bond strength specimens were etched with 5% hydrofluoric acid followed by application of a silane-containing primer (Clearfil Ceramic Primer). A Tygon tube filled with resin cement (Panavia SA) was fixed to the surface of the ceramics and light-polymerized. After 1 day or 150 days of water storage, the resin cement was debonded in a macroshear test (n=10). The cusps of extracted human molars were isolated and mounted into the University of Alabama at Birmingham wear-testing device. Wear testing was performed with a 20-N load for 300 000 cycles in 33% glycerin. The volumetric wear of polished zirconia, lithium disilicate, and enamel were measured along with the wear of the opposing enamel cusps using a noncontact profilometer (n=8). The data were compared by ANOVA and Tukey-Kramer analysis (α=.05). No statistical difference was seen between the bond strengths ( P =.155) or the opposing enamel wear ( P =.533) of different ceramics. A statistically signifi...
Research Topics
Paper Details
- Title
- Comparison of the mechanical properties of translucent zirconia and lithium disilicate
- DOI
- 10.1016/j.prosdent.2017.08.004
- Published
- Jan 6, 2018
- Journal
- Volume
- 120
- Issue
- 1
- Pages
- 132–137