Engineering Failure Analysis

In this work the failure analysis of the crankshaft of diesel engine was performed. Visual examination of the crankshaft fracture showed that beach marks, typical for fatigue failure were observed. Additional observations of the crack initiation zone indicated that crack origin was not covered by material defects or corrosion products. Performed hardness test of the fractured crank pin showed that large HRC values were observed in central part of the pin only. On the corner of cylindrical pin surface where the crack origin was located the hardness of material was much smaller. In order to explain the reason of premature crankshaft damage, the finite element method was utilized. The results of nonlinear static analysis showed that during work of the engine with maximum power the high stress area was located in crack initiation zone. Based on results of performed investigations it was concluded that the main reason of premature fatigue failure was high-cycle fatigue of the material in external zone of the crank pin where the small structural radius was designed. In final part of the work the recommendations for increase of the fatigue life of analyzed crankshaft were formulated.

Stress and failure analysis of the crankshaft of diesel engine