Characterization of crack propagation in mode I delamination of multidirectional CFRP laminates

During the experimental characterization of the mode I interlaminar fracture toughness of multidirectional composite laminates, the crack tends to migrate from the propagation plane (crack jumping) invalidating the tests. In an earlier numerical study [9], we reported that this problem could be eliminated by choosing the appropriate bending stiffness of the beam arms. In the current paper, six stacking sequences were defined numerically and...