The tensile behaviour of engineered cementitious composites (ECC) is highly dependent on their microstructure characteristics. To date, the strain-hardening behaviour of printed ECC in relation to its microstructure is not yet fully understood. This study presents a systematic investigation on the macroscopic mechanical properties of normal and printed ECC with various polyethylene (PE) fibre lengths (6 and 12 mm) in relation to their microstructural features in terms of pore structure characteristics, fibre orientation and fibre dispersion through a series of mechanical tests and X-ray computed tomography (CT) and backscattered electron (BSE) image acquisition, processing and analysis. Results indicate that it is desirable to use block specimens for mould-casting fabrication as contrast to printed ECC samples. The printed ECC containing 1.5 vol% 6 mm and 0.5 vol% 12 mm PE fibres by extrusion-based 3D printing exhibits unique tensile ductility of over 5% and average crack width of less than 100 μm. Regarding pore structure, normal ECC has a higher probability of large pores (over 1 mm3) than printed ECC, which would increase the risk of damage localization and lead to a significant variation in tensile properties. Besides, normal ECC with thickness of 30 mm and printed ECC possess a similar fist cracking strength as indicated by similar pore size and fracture toughness. Compared to normal ECC, printed ECC has a more uniform dispersion of PE fibres, the orientation of which is more perpendicular to the loading direction, resulting in a higher average tensile strength and strain capacity than normal ECC.

Relationship between microstructure and strain-hardening behaviour of 3D printed engineered cementitious composites