• Vo-BiVO 4 /FeOOH photoanode was prepared by hydrothermal and photodeposition treatment. • Oxygen vacancy and FeOOH cocatlayst enhance the charge transfer and separation efficiency. • Vo-BiVO 4 /FeOOH photoanode demonstrated excellent PEC performance than prsitine BiVO4. Herein, a new approach of inducing oxygen vacancy in BiVO 4 /FeOOH nanostructures is designed, where metal trichalcogenide is introduced. The strategy involves integration of Bi 2 S 3 quantum dots (QDs) in BiVO 4 /FeOOH to construct defect-rich BiVO 4 /FeOOH (denoted Vo-BiVO 4 /FeOOH) as high-performance photoanode for photoelectrochemical water oxidation. Both experimental and theoretical analysis confirm that the excellent PEC performance is due to the introduction of oxygen vacancies and FeOOH cocatalyst, which significantly improves the charge separation. As a result, the obtained Vo-BiVO 4 /FeOOH photoanode not only demonstrates an optimized Photoelectrochemical (PEC) performance for water oxidation, with photocurrent density of 4.71 mA cm −2 at 1.23 V versus RHE under AM 1.5 G illumination but the interaction of BiVO 4 with FeOOH cocatlayst also significantly enhance the stability for Vo-BiVO 4 /FeOOH without any decrease after 11 h. The oxygen vacancy and FeOOH can effectively enhance the light conversion efficiency, charge transfer efficiencies and charge separation efficiency. This work highlights an effective strategy towards achieving efficient and stable BiVO 4 photoanode for sustainable solar energy conversion.

Amorphous type FeOOH modified defective BiVO4 photoanodes for photoelectrochemical water oxidation