Bilayer

Engineering

Oxide

Electrochemistry

Metallurgy

Materials science

Chromatography

Layer (electronics)

Biochemistry

Inorganic chemistry

Chemical engineering

Hydroxide

Physical chemistry

Polarization (electrochemistry)

Secondary ion mass spectrometry

Chloride

Nanotechnology

Organic chemistry

Membrane

Pitting corrosion

X-ray photoelectron spectroscopy

Composite material

Analytical Chemistry (journal)

Corrosion

Chemistry

Electrode

Austenitic stainless steel

Electrolyte

Passivation

Electrochimica Acta

Electrochemical polarization measurements were combined with surface analysis by Time of Flight Secondary Ion Mass Spectroscopy (ToF-SIMS), X-Ray Photoelectron Spectroscopy (XPS) and Atomic Force Microscopy (AFM) to study the alterations of the passive film on 316L austenitic stainless steel induced by the presence of chlorides in sulfuric acid electrolyte. The work was performed at a stage of initiation of localized corrosion preceding metastable pitting at the micrometer scale as verified by current transient analysis and AFM. The results show that Cl-ions enter the bilayer structure of the surface oxide already formed in the native oxide-covered initial surface state at concentrations below the detection limit of XPS (< 0.5 at%), mostly in the hydroxide outer layer where Fe(III) and Mo(IV,VI) species are concentrated but barely in the oxide inner layer enriched in Cr(III). Their main effect is to produce a less resistive passive state by poisoning dehydroxylation and further Cr(III) and Mo(IV,VI) enrichments obtained in the absence of chlorides. This detrimental effect can be suppressed by pre-passivation in a Cl-free electrolyte, which blocks the entry of chlorides in the passive film, including in the outer exchange layer, and enables the beneficial aging-induced variations of the composition to take place despite the presence of chlorides in the environment.

Chloride-induced alterations of the passive film on 316L stainless steel and blocking effect of pre-passivation