Due to the intrinsic properties of tungsten, such as high melting point and high thermal conductivity, selective laser melting of pure W parts experiences many challenges. In this study, the effects of volumetric energy density on the densification behavior, microstructure evolution and mechanical performances of SLM-processed pure tungsten parts were investigated. A maximum density of 19.0 g/cm3 (98.4% of the theoretical density) was obtained at the optimal energy density of 1000 J/mm3 and its microstructure was free of pores and balling phenomenon. The formation mechanism of pores and cracks was systematically investigated. The microhardness and compressive strength of SLM-processed pure W parts reached 474 HV and 902 MPa, respectively, which were comparable to the samples produced by conventional manufacturing methods. The morphology of fracture demonstrated that the fracture mechanism of SLM-processed pure W parts was brittle fracture and intergranular fracture was the main fracture mode. Dry sliding wear tests showed that the wear mechanism changed with the energy density. For pure W parts processed by SLM at the optimal parameters, the adhesion of hardened tribolayers was formed. In this case, the reduced coefficient of friction (COF) of 0.45 and a low wear rate of 1.3 × 10−5 mm3·N−1·m−1 were obtained.

Selective laser melting additive manufacturing of pure tungsten: Role of volumetric energy density on densification, microstructure and mechanical properties