Ti-55531 (Ti-5Al-5Mo-5V-3Cr-1Zr) is near β titanium alloy, which plays a significant role in manufacturing landing gears and flap tracks in the aerospace industry. This study aims to find out an optimal heat treatment to obtain an excellent balance of strength, ductility and fracture toughness. For this purpose, the Ti-55531 alloy was subjected to solution plus aging treatments and mechanical properties tests. Optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM) were adopted to observe the microstructural evolution including morphology, distribution and size. Standard tensile and compact tension (CT) tests were carried out to obtain the yielding/tensile strength (YS, TS), elongation (EL) and fracture toughness (KIC) of Ti-55531 alloy. The effects of solution temperature, aging temperature and time on the microstructural evolution and fractography were analyzed. The relationships between the mechanical properties and microstructures were qualitatively described. The influencing mechanism of plastic deformation and crack propagation path on the KIC were discussed. Simultaneously, the values of YS and KIC were predicted based on mechanical property models, the predicted values were compared with tested data. Finally, an optimal heat treatment was proposed for the Ti-55531 alloy, to obtain a good balance of strength, ductility and fracture toughness.

Microstructural evolution, mechanical properties and fracture toughness of near β titanium alloy during different solution plus aging heat treatments