Collagen-based scaffolds are appealing products for the repair of cartilage defects using tissue engineering strategies. The present study investigated the collagen scaffolds with and without 1-ethyl-3-(3-dimethyl aminopropyl) carbodiimide (EDC)/N-hydroxysuccinimide (NHS)-crosslinking. Crosslinking density, matrix morphology, swelling ratio shrinkage temperature and resistance against collagenase digestion were determined to evaluate the physicochemical properties of the collagen matrices with and without crosslinking. The results conformed that the porous structure of collagen was largely preserved and adjusted by crosslinking treatment. Furthermore, crosslinked collagen samples showed significantly reduced swelling ratio and increased resistance against thermal treatment and enzymatic degradation compared to non-crosslinked samples. An in vitro evaluation of MC3T3-E1 cells seeded onto the crosslinked and non-crosslinked collagen matrix indicated that crosslinked collagen was nontoxic and improved cell proliferation. Through this work, it was shown that an osteoconductive collagen matrix with optimized properties used as bioactive and bioresorbable scaffolds in bone tissue engineering could be fabricated through the EDC/NHS-crosslinking method.

Enhanced physicochemical properties of collagen by using EDC/NHS-crosslinking