Thermal barrier coatings failure mechanism during the interfacial oxidation process under the interaction between interface by cohesive zone model and brittle fracture by phase-field

Volume: 214-215, Pages: 18 - 34
Published: Apr 1, 2021
Abstract
Failure of Thermal barrier coatings (TBCs) caused by interface oxidation directly determines the ultimate durability of TBCs. The interfacial delamination and brittle fracture will co-occur during the interface oxidation of the TBCs. To study the interaction between the two failure modes, we develop a thermodynamically-consistent coupling framework combining the phase-field model of the brittle fracture in the bulk material and the cohesive zone...
Paper Details
Title
Thermal barrier coatings failure mechanism during the interfacial oxidation process under the interaction between interface by cohesive zone model and brittle fracture by phase-field
Published Date
Apr 1, 2021
Volume
214-215
Pages
18 - 34
Citation AnalysisPro
  • Scinapse’s Top 10 Citation Journals & Affiliations graph reveals the quality and authenticity of citations received by a paper.
  • Discover whether citations have been inflated due to self-citations, or if citations include institutional bias.