Interfacial microstructure evolution and formation process of the joints prepared by diffusion bonding on DD6 nickel-based single crystal superalloy

Nickel-based single crystal superalloy DD6 was diffusion bonded in vacuum at 1170 °C under 55 MPa for 2–6 h. Two processes, direct bonding and bonding with interlayer, were designed for comparison. A pure 4 μm nickel (Ni) foil was selected for the interlayer. The joint strength was measured via shear test, whereas the joint microstructure and element distribution were analyzed via scanning electron microscope, electron probe analyzer and...