Investigation of the retained austenite orientation in iron precipitates of martensitic transformation
Abstract
The retained austenite orientation in iron precipitates of martensitic transformation was studied in a Cu-Fe-P alloy. The alloy was isochronally aged at 723 K with tensile stresses of 0 and 16 MPa after solution treatment at 1143 K for 2 h respectively. The results showed that [220]γ-Fe and [200]γ-Fe of austenite (γ-Fe) in iron precipitates was parallel to [220]Cu and [200]Cu of copper matrix during ageing without applied stress, respectively....
Paper Details
Title
Investigation of the retained austenite orientation in iron precipitates of martensitic transformation
Published Date
Dec 1, 2020
Journal
Volume
280
Pages
128556 - 128556
Citation AnalysisPro
You’ll need to upgrade your plan to Pro
Looking to understand the true influence of a researcher’s work across journals & affiliations?
- Scinapse’s Top 10 Citation Journals & Affiliations graph reveals the quality and authenticity of citations received by a paper.
- Discover whether citations have been inflated due to self-citations, or if citations include institutional bias.
Notes
History