Application of the eutectic high entropy alloy Nb0.73CoCrFeNi2.1 for high temperature joints

The eutectic high entropy alloy Nb0.73CoCrFeNi2.1 was manufactured by means of arc smelting and the obtained ingots were cut into 300-μm-thick foils, which were used as filler alloys to braze Crofer 22 APU to Hf-metallized yttria-stabilized zirconia (3YSZ). The brazing process was conducted in a vacuum furnace at 1200 °C for 5 min at a vacuum of 4.3·10–4 mbar. In order to minimize the intense diffusion and erosion of the steel substrate, a...