Creep rupture ductility of Gr.91 and Gr.92 at 550°C to 700°C

The creep rupture ductility has been investigated for Gr.91 and Gr.92 at 550 to 700°C for up to 118,648.8 h. The degradation in the reduction of area (RA) is more significant in Gr.92 than in Gr.91 at 550°C to 700°C. The boron nitride particles are responsible for the degradation in RA in Gr.92 at long times by accelerating the formation of creep voids. The creep ductility parameter λ decreases to small values below 5 for Gr.92 at long times at...