International Journal of Fatigue

Laser Shock Peening is a surface treatment technique used in the aerospace sector to increase fatigue life, as well as resistance to fretting fatigue and stress corrosion cracking. In this study, laser shock peening was applied to a 6-mm-thick middle-crack tension specimen made of aluminium 2524-T351. Residual stress was measured with neutron diffraction and the contour method, along the predicted crack path prior to fatigue testing. Fatigue crack growth test results showed that fatigue life improved by a factor of 4 compared to an untreated component, owing to a significant crack growth rate reduction inside the laser peened area. A linear-elastic finite-element crack growth prediction model was also developed, obtaining predicted results in excellent agreement with the experimental data.

Fatigue crack growth in a laser shock peened residual stress field