Damage and failure mechanism of thin composite laminates under low-velocity impact and compression-after-impact loading conditions

Impact resistance and damage tolerance are of great significance in the design of composite structures. This study investigated the damage and failure mechanism of thin composite laminates under low-velocity impact and compression-after-impact (CAI) loading conditions. Four levels of impact energy were included in the test matrix. Delamination induced by low-velocity impact was captured using ultrasonic C-scan, and a three-dimensional (3D)...