Interlaminar crack onset in co‐cured and co‐bonded composite joints under mode I cyclic loading

Composite joints exhibit different behavior in regard to delamination resistance when dealing with fatigue phenomenon. This research work focuses on an investigation to understand the failure mechanisms on the interfacial strength domain for delamination onset in cocured and cobonded joints. The analysis was based on strain energy release rate versus number of cycles plots that were obtained from fatigue tests in mode I with a stress ratio R =...