Effect of stress ratios on tension–tension fatigue behavior and micro-damage evolution of basalt fiber-reinforced epoxy polymer composites

The tension–tension fatigue behavior and damage mechanism of basalt fiber-reinforced epoxy polymer (BFRP) composites at different stress ratios are studied in this paper. The fatigue experiments were performed under stress ratios, R = σmin/σmax of 0.1 and 0.5, while the lifetime and the stiffness degradation were monitored and analyzed to investigate the effect of stress ratios. The damage propagation during fatigue loading was periodically...