Microstructural Evolution in a 9%Cr-3%Co-3%W-VNb Steel during Creep

Microstructural evolution in a 9Cr-3Co-3W-0.2V-0.06Nb-0.05N-0.005B steel crept at T=650°C under an applied stress of 140 MPa up to strains of 1, 3, 5.75 and 12%, which represent primary, secondary and tertiary creep stages and rupture, respectively, was studied. The steel was initially normalized from 1050°C, and finally tempered at 750°C for 3h. After tempering the boundaries of tempered martensite lath structure (TMLS) were decorated by M 23 C...