Microstructure evolution in HR3C austenitic steel during long-term creep at 650°C

The creep behavior of HR3C austenitic steels was investigated at 650 °C and over the stress range from 150 to 250 MPa for up to 13,730 h. The corresponding microstructure evolution was characterized by optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). In the initial stage of the creep process, the creep-resistance of HR3C steel is enhanced by the precipitation of second-phases particles in...