Effect of temperature gradient on the erosion behavior of SiC coating for carbon/carbon composites in a combustion environment

SiC coating with a thickness of 50–70 µm was prepared on the surface of C/C composites by in-situ reaction method. The SiC coated C/C composites were then tested in a wind tunnel where a temperature gradient from 200 to 1600 °C could be obtained to investigate their erosion behavior. The results of wind tunnel test indicated that the service life of C/C composites was prolonged from 0.5 to 44 h after applying the SiC coating. After the wind...