Developing Dislocation Subgrain Structures and Cyclic Softening During High-Temperature Creep–Fatigue of a Nickel Alloy

The complex cyclic deformation response of Alloy 617 under creep–fatigue conditions is of practical interest both in terms of the observed detriment in failure life and the considerable cyclic softening that occurs. At the low strain ranges investigated, the inelastic strain is the sole predictor of the failure life without taking into consideration a potentially significant environmental influence. The tensile-hold creep–fatigue peak stress...