Microstructural degradation of Gr.91 steel during creep under low stress

Microstructural changes during creep at 600 °C under 70 MPa were investigated in the case of interrupted Gr.91 steel samples by taking into account the dislocation structure and Z-phase formation. The creep life monotonically increased with a decrease in the applied stress at each temperature considered in the study. However, the long-term creep life was shorter than that determined from the short-term creep data at 600 °C and 650 °C, meaning...