Tensile properties of an AlCrCuNiFeCo high-entropy alloy in as-cast and wrought conditions

Extensive multistep forging at 950 °C was applied to the cast AlCuCrFeNiCo high-entropy alloy to transform the cast coarse dendritic structure into a fine equiaxed duplex structure consisting of the mixture of BCC and FCC phases, with the average grain/particle size of ∼1.5 ± 0.9 μm. Tensile properties of the alloy in the as-cast and forged conditions were determined in the temperature range of 20–1000 °C. The hot forged alloy was stronger and...