Failure analysis of triaxial braided composite

This study focuses on the description of damage and failure behaviour of triaxial braided carbon/epoxy composites under tension. The tensile tests were instrumented with optical surface strain and acoustic emission measurements. Damage was observed using X-ray and microscopy. The damage develops in two stages: (1) intra-yarn cracking: increase of the crack density and crack length, (2) local inter-yarn delamination and conjunction of the...